Metal Finishing Guide Book

2012-2013

Issue link: https://metalfinishing.epubxp.com/i/98750

Contents of this Issue

Navigation

Page 399 of 903

Final Finish Applied Hours to White Corrosion None/passivate only 24���48 h Tridur Finish 300 (20% v/v) 312 h Corrosil Plus 501 BG* 432 h *Organic polymer/silicate-based sealer. Table 3: Minimum Corrosion Resistance of Different Finishes Applied to Black Passivated Zinc-Nickel (Tridur ZnNi H1): Neutral Salt Spray Testing (ISO 9227). Conversion Coating conversion coating. Figure 9 shows a structural proposal for this layer���s composition. Polynuclear chromium(III) complexes bearing ��-phosphato bridges are described in literature10���12 and they most likely contribute to the post-dip layer���s composition. Due to the very similar composition of Tridur Finish 300 layers and passivate F/Nm T/kN KM10 ��thread ��head ��tot Tridur Zn H1 120.3 �� 11.3 36.1 �� 0.01 0.33 �� 0.03 0.32 �� 0.04 0.22 �� 0.04 0.27 �� 0.03 Tridur ZnNi H1 150.9 �� 13.7 36.1 �� 0.02 0.42 �� 0.04 0.33 �� 0.07 0.35 �� 0.03 0.34 �� 0.03 Table 4: Friction Properties Determined on M10��50 Bolts (measurements �� standard deviation) layers, it is very difficult to find some contrast between both layers by means of SEM imaging. However, Figure 10 shows an SEM image of a FIB cross section through a sample with Tridur Finish 300 applied to black passivated zinc���nickel (14% nickel). The image reveals a thickness of 100���200 nm for the passivate and the post-dip layer. Layer morphology. The morphology of the post-dip layer was investigated using different concentrations of Tridur Finish 300 applied to a black passivated (Tridur ZnNi H1) zinc���nickel alloy surface. The morphology of the deposit in dependence of the concentration of the post-dip bath was studied by means of SEM micrographs on samples of black passivated zinc���nickel (Figs. 11���14). The post-dip caulks the micro cracks of the black passivated zinc���nickel surface. The post-dip layer���s appearance itself resembles that observed with a hexavalent black chromate on zinc���nickel with regard to the mud-crack-like surface observed. Above 200 ml/l the post-dip layer���s cracks become larger in size (Fig. 15). This means that with excessive concentrations a lesser extent of the surface may be covered by the post-dip layer. No significant advantage concerning neither the aspect nor the corrosion protection could be determined with higher concentrations. Corrosion-protection properties. Corrosion-protection properties were investigated with different concentrations of the post-dip solutions (Tridur Finish 300) applied to black passivated zinc���nickel. It was found that a high level of corrosion protection was already established with 50 ml/l of Tridur Finish 300, not increasing significantly with higher concentrations (100���300 ml/l). However, the aspect of the parts finished was found to be best at 200 ml/l (20% v/v). Evaluation on black passivated zinc���iron (Tridur ZnFe H1) produced similar results. On black passivated zinc (Tridur Zn H1), 100 ml/l was found to be a suitable concentration. With regard to the decorative aspect of the finished surfaces as well as their corrosion-protection properties by means of neutral salt spray testing, the applica392

Articles in this issue

view archives of Metal Finishing Guide Book - 2012-2013